Certification: | RoHS, UL, ISO9001, CE |
---|---|
Type: | Electric Coil |
Form: | Heating Wire |
Shape: | Tubular |
Type.: | Electrothermal Ceramics |
Leads: | Ceramic Biomass Igniter |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
1
|
Part No.
|
JORY910
|
2
|
Usage
|
ignition
|
3
|
Working Voltage
|
120 V / 230V
|
4
|
Power
|
150W, 180W, 210W, 225W, 230W, 240W, 255W
|
5
|
Dimension of product
|
Existing Sample:OD10.5*ID6.2*90MM,Holder Size:D17.5*35MM
|
Cable Wire Length:500mm
|
||
Customized sample is acceptable
|
||
6
|
Electrode
|
Welding leads on the electrode
|
7
|
Advantages
|
(1)Ready to fit solution: High temperature heating element in temperature-resistant ceramic socket
|
(2)Air can flow through and around inside and outside of heater
|
||
(3)Element temperature: over 1000 °C in permanent and alternating operation, for a short time up to 1200 °C
|
||
(4)Lifetime up to 100,000 heating cycles, depending on operating conditions
|
||
(5)Oxidation and corrosion-resistant
|
||
(6)Ignition through air heating: Due to extremely high heater temperature and ideal geometric conditions, air is heated in a very
short time to very high temperatures - the ideal ignition blower! |
||
(7)Igniting wood chips, firewood, coal bricks or other biomass (corn, etc.) is possible.
|
Thermal Properties for Alumina Heater
|
||
Item
|
Unit
|
Value
|
Vickers Hardness
|
Gpa
|
11.5
|
Flexural Strength
|
Mpa
|
300
|
Compressive Strength
|
Mpa
|
2000
|
Modulus of Elasticity
|
Gpa
|
300
|
Poisson's Ratio
|
---
|
0.22-0.23
|
Fracture Toughness
|
Mpam1/2
|
3.5-4.0
|
Thermal Conductivity
|
W/(m·k)
|
25
|
Thermal Expansion Coefficient
|
10-6/ºC
|
6.5-7.5
|
Thermal Shock Resistance
|
△TºC
|
200
|
Maximum Use Temperature
|
ºC
|
1600
|
Dielectric Strength
|
KV/mm
|
>12
|
Dielectric Constant
|
εr
|
9-10
|
Dielectric Loss Angle (1MHz)
|
---
|
0.0002
|
Volume Resistivity
|
Ω.m
|
>1015
|
Specific Heat
|
J/(kg·k)
|
0.78x103
|
Our Certificate
ISO 9000; RoHS REACH
Inspection Standard
To ensure the quality of products, the in-process inspection and sampling inspection should be taken which based on the regulation of National GB/T 2828-2003.
Part 1.Sampling inspection of AQL standard.
In-process inspection VS Sampling Inspection
Inspection items |
In-process inspection |
QC sampling inspection |
|
Inspection level |
Acceptable quality level (AQL) |
||
Appearance |
100% inspection |
|
1.0 |
Straightness |
100% inspection |
S-4 |
1.0 |
Dimension |
100% inspection |
|
1.0 |
Power-on Test |
100% inspection |
|
0.40 |
Dielectric Strength |
100% inspection |
|
0.65 |